خواص مکانیکی
(Charpy Impact Strength(unnotched۹۹٬۹۹۰ISO 179/1eU, Temperature 0 °CkJ/m2
Hardness Shore D۸۰ISO 868
(Charpy Impact Strength(notched۱۴ISO 179/1eA, Temperature 23 °CkJ/m2
Elongation at yield۹5mm/min, Outer fiber strain at maximum stress; ISO 178%
Tensile modulus-MD۱٬۴۰۰ISO 527-1/2MPa
Tensile strength>50at Break, 50 mm/min ; ISO 527-1/2MPa
Ball indentation Hardness۱۱۰H30; ISO 2039-1MPa
Elongation at break-MD>15050mm/min ; ISO 527-1/2%
Flexural strength۹۰5mm/min; ISO 178MPa
Flexural modulus-MD۱٬۶۵۰ISO 178MPa
(Charpy Impact Strength(unnotched۹۹٬۹۹۰ISO 179/1eU, Temperature 23°CkJ/m2
(Charpy Impact Strength(notched۱۳ISO 179/1eA, Temperature -30°CkJ/m2
Elongation at yield۸50mm/min ; ISO 527-1/2%
Tensile strength۶۰at Yield, 50 mm/min ; ISO 527-1/2MPa
Flexural strength۵۰5mm/min, at 3.5% Strain; ISO 178MPa
(Charpy Impact Strength(unnotched۹۹٬۹۹۰ISO 179/1eU, Temperature -30°CkJ/m2
(Charpy Impact Strength(notched۱۴ISO 179/1eA, Temperature 0°CkJ/m2