XR409HJ ABS, Heat Resistance, Curl Fit | Metasan
Home
/
Products
/
ABS
/ XR409HJ ABS, Heat Resistance, Curl Fit
XR409HJ ABS, Heat Resistance, Curl Fit
An acrylonitrile butadiene styrene (ABS) grade. It is suitable for processing through injection molding.
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
Applications
Automotives Interior & Exterior Housing (P/W Switch Housing Etc)
Advantages
Heat Resistance
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Physical Properties
Specific Gravity
1.06
ASTM D792
Melting range
220 – 240
قالب گیری تزریقی
°C
Processing Properties
Linear Mold Shrinkage
0.004 – 0.007
ASTM D955;(Flow), 3.2mm
cm/cm
MFI
5
ASTM D1238;220℃/10kg
g/10min
Drying Temperature
80 – 90
قالب گیری تزریقی
°C
Dry Time
180 – 240
قالب گیری تزریقی
min
Mold Temperature
60 – 80
قالب گیری تزریقی
°C
Middle Barrel Temperature
220 – 230
قالب گیری تزریقی
°C
Mechanical Properties
Rockwell Hardness
105
ASTM D785;Rockwell R
Tensile Stress at yield-MD
47.1
ASTM D638;50mm/min;3.2mm
MPa
Elongation at break-MD
20
ASTM D638;50mm/min;3.2mm
%
Flexural strength
76.5
ASTM D790;15mm/min;3.2mm;Yield
MPa
Flexural modulus-MD
2,450
ASTM D790;15mm/min;3.2mm
MPa
Izod impact strength (notched)
118
ASTM D256;23℃;6.4mm
J/m
Izod impact strength (unnotched)
58.8
ASTM D256;-30℃;6.4mm
J/m
Izod impact strength (notched)
127
ASTM D256;23℃;3.2mm
J/m
Izod impact strength (unnotched)
68.6
ASTM D256;-30℃;3.2mm
J/m
Thermal Properties
Heat Deflection temperature
114
Unannealed; ASTM D648;Thickness 6.40 mm;at 0.46 MPa
°C
Vicat softening temperature
112
ASTM D1525;5kg, 50℃/h
°C
Heat Deflection temperature
105
Unannealed; ASTM D648;Thickness 6.40 mm;at 1.8 MPa
°C
Chemical Properties
Humidity content
<0.01
قالب گیری تزریقی
%