XG570 MABS, Anti-Scratch, High Impact, High Flow
An acrylonitrile butadiene styrene (ABS) grade. It is suitable for processing through injection molding.
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
CAS number
9010-94-0
Applications
LCD TV Stand Base Audio/Video Housing
Advantages
Anti-Scratch High Impact High Flow
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Physical Properties
Specific Gravity
1.06
ASTM D792
Melting range
200 – 230
قالب گیری تزریقی
°C
Processing Properties
Linear Mold Shrinkage
0.004 – 0.006
ASTM D955;(Flow), 3.2mm
cm/cm
MFI
22
ASTM D1238;220℃/10kg
g/10min
Drying Temperature
80 – 90
قالب گیری تزریقی
°C
Dry Time
180 – 240
قالب گیری تزریقی
min
Mold Temperature
40 – 60
قالب گیری تزریقی
°C
Middle Barrel Temperature
180 – 200
قالب گیری تزریقی
°C
Mechanical Properties
Rockwell Hardness
115
ASTM D785;Rockwell R
Tensile Stress at yield-MD
49
ASTM D638;50mm/min;3.2mm
MPa
Elongation at break-MD
30
ASTM D638;50mm/min;3.2mm
%
Elongation at yield
>6
ASTM D638;50mm/min;3.2mm
%
Flexural strength
82.4
ASTM D790;15mm/min;3.2mm;Yield
MPa
Flexural modulus-MD
2,890
ASTM D790;15mm/min;3.2mm
MPa
Izod impact strength (notched)
177
ASTM D256;23℃;6.4mm
J/m
Izod impact strength (unnotched)
98.1
ASTM D256;-20℃;6.4mm
J/m
Izod impact strength (notched)
177
ASTM D256;23℃;3.2mm
J/m
Izod impact strength (unnotched)
98.1
ASTM D256;-20℃;3.2mm
J/m
Chemical Properties
Humidity content
<0.01
قالب گیری تزریقی
%
Water absorption
0.3
ASTM D570;Temperature 23.0°C, Time 86400 sec
%
Thermal Properties
Heat Deflection temperature
87
Unannealed; ASTM D648;at 1.8 MPa;Thickness 6.40 mm
°C
Flameability
HB
UL94;Thickness >=1.60 mm
Heat Deflection temperature
87
Unannealed; ASTM D648;at 1.8 MPa;Thickness 3.20 mm
°C
Flameability
HB
UL94;Thickness >=3.20 mm
Heat Deflection temperature
91
ASTM D648;at 1.8 MPa;Thickness 6.40 mm
°C
Heat Deflection temperature
91
ASTM D648;at 1.8 MPa;Thickness 3.20 mm
°C