XG568 MABS, Anti-Scratch, High Gloss | Metasan
Home
/
Products
/
ABS
/ XG568 MABS, Anti-Scratch, High Gloss
XG568 MABS, Anti-Scratch, High Gloss
An acrylonitrile butadiene styrene (ABS) grade. It is suitable for processing through injection molding.
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
Applications
LCD TV Front Cabinet Bezel Audio/Video Housing
Advantages
Anti-Scratch High Gloss
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Physical Properties
Specific Gravity
1.11
ASTM D792
Melting range
200 – 230
قالب گیری تزریقی
°C
Processing Properties
Linear Mold Shrinkage
0.002 – 0.004
ASTM D955;(Flow), 3.2mm
cm/cm
MFI
19.5
ASTM D1238;220℃/10kg
g/10min
Drying Temperature
80 – 90
قالب گیری تزریقی
°C
Dry Time
180 – 240
قالب گیری تزریقی
min
Mold Temperature
40 – 60
قالب گیری تزریقی
°C
Middle Barrel Temperature
190 – 210
قالب گیری تزریقی
°C
Mechanical Properties
Rockwell Hardness
114
ASTM D785;Rockwell R
Tensile Stress at yield-MD
53
ASTM D638;50mm/min;3.2mm
MPa
Elongation at break-MD
20
ASTM D638;50mm/min;3.2mm
%
Elongation at yield
>6
ASTM D638;50mm/min;3.2mm
%
Flexural strength
85.3
ASTM D790;15mm/min;3.2mm;Yield
MPa
Flexural modulus-MD
2,750
ASTM D790;15mm/min;3.2mm
MPa
Izod impact strength (notched)
88.3
ASTM D256;23℃;6.4mm
J/m
Izod impact strength (unnotched)
39.2
ASTM D256;-20℃;6.4mm
J/m
Izod impact strength (notched)
88.3
ASTM D256;23℃;3.2mm
J/m
Izod impact strength (unnotched)
39.2
ASTM D256;-20℃;3.2mm
J/m
Chemical Properties
Humidity content
<0.01
قالب گیری تزریقی
%
Water absorption
0.3
ASTM D570;Temperature 23.0°C, Time 86400 sec
%
Thermal Properties
Heat Deflection temperature
86
ASTM D648;Thickness 3.20 mm;at 0.46 MPa
°C
Flameability
HB
UL94;Thickness >=1.60 mm
Heat Deflection temperature
88
Unannealed; ASTM D648;Thickness 6.40 mm;at 0.46 MPa
°C
Flameability
HB
UL94;Thickness >=3.20 mm
Heat Deflection temperature
82
ASTM D648;Thickness 3.20 mm;at 1.8 MPa
°C
Heat Deflection temperature
83
Unannealed; ASTM D648;Thickness 6.40 mm;at 1.8 MPa
°C