SH610A ABS, High Impact | Metasan
Home
/
Products
/
ABS
/ SH610A ABS, High Impact
SH610A ABS, High Impact
An acrylonitrile butadiene styrene (ABS) grade. It is suitable for processing through extrusion molding.
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
CAS number
9003-56-9
Applications
Bag Automobile Interior
Advantages
General Purpose High Impact
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Processing Properties
MFI
1
ASTM D1238;230℃/3.50kg
g/10min
Drying Temperature
70 – 80
قالب گیری اکستروژنی
°C
Dry Time
180 – 240
قالب گیری اکستروژنی
min
Processing Temperature
180 – 210
قالب گیری اکستروژنی، ناحیه 1
°C
Die Temperature
200 – 250
قالب گیری اکستروژنی
°C
Linear Mold Shrinkage
0.004 – 0.007
ASTM D955;(Flow), 3.2mm
cm/cm
Processing Temperature
190 – 230
قالب گیری اکستروژنی، ناحیه2
°C
Processing Temperature
200 – 250
قالب گیری اکستروژنی، ناحیه3
°C
Processing Temperature
200 – 250
قالب گیری اکستروژنی، ناحیه4
°C
Mechanical Properties
Rockwell Hardness
97
ASTM D785;Rockwell R
Tensile Stress at yield-MD
42.2
ASTM D638;50mm/min;3.2mm
MPa
Elongation at break-MD
35
ASTM D638;50mm/min;3.2mm
%
Elongation at yield
>5
ASTM D638;50mm/min;3.2mm
%
Flexural strength
63.7
ASTM D790;15mm/min;3.2mm;Yield
MPa
Flexural modulus-MD
1,960
ASTM D790;15mm/min;3.2mm
MPa
Izod impact strength (notched)
422
ASTM D256;23℃;6.4mm
J/m
Izod impact strength (notched)
490
ASTM D256;23℃;3.2mm
J/m
Thermal Properties
Heat Deflection temperature
92
ASTM D648;6.4mm;(Unannealed);at 0.46MPa
°C
Vicat softening temperature
94
ASTM D1525;5kg, 50℃/h
°C
UL RTI
60
UL 746B;Thickness >=1.50 mm;Electrical
°C
Flameability
HB
UL94;Thickness >=1.50 mm
Heat Deflection temperature
87
ASTM D648;6.4mm;(Unannealed);at 1.8 MPa
°C
UL RTI
60
UL 746B;Thickness >=1.50 mm;Mechanical with Impact
°C
UL RTI
60
UL 746B;Thickness >=1.50 mm;Mechanical without Impact
°C
Chemical Properties
Humidity content
<0.01
قالب گیری اکستروژنی
%
Physical Properties
Melting range
200 – 250
قالب گیری اکستروژنی
°C
Specific Gravity
1.04
ASTM D792