LUMAX GP5106FI PBT+ABS+GF10%, Flame Retardant | Metasan
Home
/
Products
/
Polyesters
/
ABS
/
Glass fiber
/ LUMAX GP5106FI PBT+ABS+GF10%, Flame Retardant
LUMAX GP5106FI PBT+ABS+GF10%, Flame Retardant
Acrylonitrile butadiene styrene (ABS) /Polybutylene Terephthalate (PBT) alloy with 10% Glass Fiber. It is suitable for processing through injection molding.
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
Applications
Electric & Electronic Products (Switch)
Advantages
Flame Retardant Impact Modified Dimensional Stability
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Physical Properties
Specific Gravity
1.4
ASTM D792
Melting range
240 – 250
قالب گیری تزریقی
°C
Melting point
225
Peak at Break
°C
Processing Properties
Linear Mold Shrinkage
0.004 – 0.009
ASTM D955;(Flow), 3.2mm
cm/cm
Drying Temperature
100
قالب گیری تزریقی
°C
Mold Temperature
60 – 90
قالب گیری تزریقی
°C
Middle Barrel Temperature
230 – 245
قالب گیری تزریقی
°C
Mechanical Properties
Tensile Stress at yield-MD
55.9
ASTM D638;5mm/min;3.2mm
MPa
Elongation at break-MD
3
ASTM D638;5mm/min;3.2mm
%
Flexural strength
83.4
ASTM D790;1.3mm/min;3.2mm;Yield
MPa
Flexural modulus-MD
2,940
ASTM D790;1.3mm/min;3.2mm
MPa
Izod impact strength (notched)
58.8
ASTM D256;23℃;3.2mm
J/m
Thermal Properties
Heat Deflection temperature
110
ASTM D648;6.4mm;(Unannealed);at 1.8 MPa
°C
UL RTI
60
Thickness >=1.50 mm;Electrical
°C
Flameability
V-0
UL94;Thickness >=1.50 mm
UL RTI
60
Thickness >=3.00 mm;Electrical
°C
Flameability
V-0
UL94;Thickness >=3.00 mm
UL RTI
60
Thickness >=1.50 mm;Mechanical with Impact
°C
UL RTI
60
Thickness >=3.00 mm;Mechanical with Impact
°C
UL RTI
60
Thickness >=1.50 mm;Mechanical without Impact
°C
UL RTI
60
Thickness >=3.00 mm;Mechanical without Impact
°C
Chemical Properties
Humidity content
<0.02
قالب گیری تزریقی
%
Electrical Properties
Volume resistance
1,000,000,000,000,000
ASTM D257
ohm-cm
Dielectric Strength
26
ASTM D149;Thickness 1.00 mm
kV/mm
Comparative Tracking Index
175
Solution A; IEC 60112
V
Arc Resistance
60 – 120
ASTM D495
s
Hot Wire Ignition
15 – 30
Thickness >=1.50 mm
s
HAI)High Amp Arc Ignition)
60 – 120
Thickness 1.50 mm
arcs
Hot Wire Ignition
30 – 60
Thickness >=3.00 mm
s
HAI)High Amp Arc Ignition)
30 – 60
Thickness 3.00 mm
arcs