HF380XC ABS, High Flow, High Surface Gloss | Metasan
Home
/
Products
/
ABS
/ HF380XC ABS, High Flow, High Surface Gloss
HF380XC ABS, High Flow, High Surface Gloss
An acrylonitrile butadiene styrene (ABS) grade. It is suitable for processing through injection molding.
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
CAS number
9003-56-9
Applications
large and complicated part
Advantages
High Flow High Surface Gloss High thermal stability
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Physical Properties
Specific Gravity
1.04 – 1.07
ASTM D792
Melting range
210 – 240
قالب گیری تزریقی
°C
Processing Properties
Linear Mold Shrinkage
0.004 – 0.007
ASTM D955;(Flow), 3.2mm
cm/cm
MFI
40
ASTM D1238;220℃/10kg
g/10min
Drying Temperature
80
قالب گیری تزریقی
°C
Dry Time
120 – 240
قالب گیری تزریقی
min
Mold Temperature
40 – 70
قالب گیری تزریقی
°C
Middle Barrel Temperature
190 – 210
قالب گیری تزریقی
°C
Mechanical Properties
Rockwell Hardness
109
ASTM D785;Rockwell R
Tensile Stress at yield-MD
43.1
ASTM D638;50mm/min;3.2mm
MPa
Elongation at break-MD
>7
ASTM D638;50mm/min;3.2mm
%
Elongation at yield
>3
ASTM D638;50mm/min;3.2mm
%
Flexural strength
68.6
ASTM D790;15mm/min;3.2mm;Yield
MPa
Flexural modulus-MD
2,450
ASTM D790;15mm/min;3.2mm
MPa
Izod impact strength (notched)
196
ASTM D256;23℃;3.2mm
J/m
Thermal Properties
Heat Deflection temperature
87
ASTM D648;6.4mm;(Unannealed);at 1.8 MPa
°C
UL RTI
60
UL 746B;Thickness >=1.50 mm;Electrical
°C
Flameability
HB
UL94;Thickness >=1.50 mm
UL RTI
60
UL 746B;Thickness >=3.00 mm;Electrical
°C
Flameability
HB
UL94;Thickness >=3.00 mm
UL RTI
60
UL 746B;Thickness >=1.50 mm;Mechanical with Impact
°C
UL RTI
60
UL 746B;Thickness >=3.00 mm;Mechanical with Impact
°C
UL RTI
60
UL 746B;Thickness >=1.50 mm;Mechanical without Impact
°C
UL RTI
60
UL 746B;Thickness >=3.00 mm;Mechanical without Impact
°C
Chemical Properties
Humidity content
<0.01
قالب گیری تزریقی
%
Electrical Properties
Volume resistance
10,000,000,000,000
ohm-cm
Dielectric Strength
34
kV/mm
Comparative Tracking Index
400 – 600
V
Arc Resistance
60 – 120
ASTM D495
s
Hot Wire Ignition
15 – 30
Thickness >=1.50 mm
s
HAI)High Amp Arc Ignition)
>120
Thickness 1.50 mm
arcs
Hot Wire Ignition
15 – 30
Thickness >=3.00 mm
s
HAI)High Amp Arc Ignition)
>120
Thickness 3.00 mm
arcs