HF380NS ABS, High Flow, General Anti-Static | Metasan
Home
/
Products
/
ABS
/ HF380NS ABS, High Flow, General Anti-Static
HF380NS ABS, High Flow, General Anti-Static
An acrylonitrile butadiene styrene (ABS) grade. It is suitable for processing through injection molding.
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
CAS number
9003-56-9
Applications
Electric & Electronic Products Miscellaneous goods
Advantages
High Flow General Anti-Static
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Physical Properties
Specific Gravity
1.04
ASTM D792
Melting range
210 – 240
قالب گیری تزریقی
°C
Processing Properties
Linear Mold Shrinkage
0.004 – 0.007
ASTM D955;(Flow), 3.2mm
cm/cm
MFI
43
ASTM D1238;220℃/10kg
g/10min
Drying Temperature
80
قالب گیری تزریقی
°C
Dry Time
120 – 240
قالب گیری تزریقی
min
Mold Temperature
40 – 70
قالب گیری تزریقی
°C
Middle Barrel Temperature
190 – 210
قالب گیری تزریقی
°C
Mechanical Properties
Rockwell Hardness
106
ASTM D785;Rockwell R
Tensile Stress at yield-MD
42.2
ASTM D638;50mm/min;3.2mm
MPa
Elongation at break-MD
40
ASTM D638;50mm/min;3.2mm
%
Flexural strength
68.6
ASTM D790;15mm/min;3.2mm;Yield
MPa
Flexural modulus-MD
2,450
ASTM D790;15mm/min;3.2mm
MPa
Izod impact strength (notched)
235
ASTM D256;23℃;6.4mm
J/m
Izod impact strength (notched)
235
ASTM D256;23℃;3.2mm
J/m
Thermal Properties
Heat Deflection temperature
84
ASTM D648;6.4mm;(Unannealed);at 1.8 MPa
°C
UL RTI
60
UL 746B;Thickness >=1.50 mm;Electrical
°C
Flameability
HB
UL94;Thickness >=1.50 mm
UL RTI
60
UL 746B;Thickness >=3.00 mm;Electrical
°C
Flameability
HB
UL94;Thickness >=3.00 mm
UL RTI
60
UL 746B;Thickness >=1.50 mm;Mechanical with Impact
°C
UL RTI
60
UL 746B;Thickness >=3.00 mm;Mechanical with Impact
°C
UL RTI
60
UL 746B;Thickness >=1.50 mm;Mechanical without Impact
°C
UL RTI
60
UL 746B;Thickness >=3.00 mm;Mechanical without Impact
°C
Chemical Properties
Humidity content
<0.01
قالب گیری تزریقی
%
Electrical Properties
Volume resistance
10,000,000,000,000
ohm-cm
Dielectric Strength
34
kV/mm
Comparative Tracking Index
400 – 600
Solution A; IEC 60112
V
Arc Resistance
60 – 120
ASTM D495
s
Hot Wire Ignition
15 – 30
Thickness >=1.50 mm
s
HAI)High Amp Arc Ignition)
>120
Thickness 1.50 mm
arcs
Hot Wire Ignition
15 – 30
Thickness >=3.00 mm
s
HAI)High Amp Arc Ignition)
>120
Thickness 3.00 mm
arcs