BM662B ABS, Heat Resistance | Metasan
Home
/
Products
/
ABS
/ BM662B ABS, Heat Resistance
BM662B ABS, Heat Resistance
An acrylonitrile butadiene styrene (ABS) grade. It is suitable for processing through Blow Molding.
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
Applications
Automotives Exterior Housing (Spoiler, Bumper Guard etc.)
Advantages
Heat Resistance
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Physical Properties
Specific Gravity
1.05
ASTM D792
Melting range
200 – 210
قالب گیری بادی
°C
Processing Properties
Linear Mold Shrinkage
0.004 – 0.007
ASTM D955;(Flow), 3.2mm
cm/cm
MFI
2
ASTM D1238;220℃/10kg
g/10min
Drying Temperature
80 – 90
قالب گیری بادی
°C
Dry Time
180 – 240
قالب گیری بادی
min
Processing Temperature
180 – 200
قالب گیری بادی، ناحیه 1
°C
Die Temperature
220
قالب گیری بادی
°C
Processing Temperature
190 – 210
قالب گیری بادی، ناحیه2
°C
Processing Temperature
190 – 210
قالب گیری بادی، ناحیه 3
°C
Processing Temperature
200 – 220
قالب گیری بادی، ناحیه 4
°C
Mechanical Properties
Rockwell Hardness
101
ASTM D785;Rockwell R
Tensile Stress at yield-MD
45.1
ASTM D638;50mm/min;3.2mm
MPa
Elongation at break-MD
30
ASTM D638;50mm/min;3.2mm
%
Flexural strength
70.6
ASTM D790;15mm/min;3.2mm;Yield
MPa
Flexural modulus-MD
2,110
ASTM D790;15mm/min;3.2mm
MPa
Izod impact strength (notched)
127
℃ 23; ASTM D256;Thickness 3.20 mm
J/m
Izod impact strength (unnotched)
68.6
℃ 30-; ASTM D256;Thickness 3.20 mm
J/m
Izod impact strength (notched)
127
℃ 23; ASTM D256;Thickness 6.40 mm
J/m
Izod impact strength (unnotched)
68.6
℃ 30-; ASTM D256;Thickness 6.40 mm
J/m
Thermal Properties
Heat Deflection temperature
108
ASTM D648;6.4mm;(Unannealed);at 0.46 MPa
°C
Vicat softening temperature
106
ASTM D1525;1kg, 120℃/h
°C
Heat Deflection temperature
100
ASTM D648;6.4mm;(Unannealed);at 1.8 MPa
°C
Chemical Properties
Humidity content
<0.01
قالب گیری بادی
%