LG Chemical HYPERIER IP1306B PA-HDPE Nanoclay Compound | Metasan
Home
/
Products
/
Polyamides
/
Poly ethylene
/ LG Chemical HYPERIER IP1306B PA-HDPE Nanoclay Compound
LG Chemical HYPERIER IP1306B PA-HDPE Nanoclay Compound
HYPERIER is a nano compound made from nano-sized inorganic plate clay. Barrier thermoplastic, Nylon blend with HDPE.
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
Applications
Blow Molding Agrochemical Container SORE Fuel Tank PFC
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Physical Properties
Specific Gravity
0.98
ASTM D792
Melting range
200 – 230
Blow Molding
°C
Processing Properties
MFI
0.35 – 0.4
ASTM D 1238, Temperature 190 °C
g/10min
Dry Time
180 – 240
Blow Molding
min
Drying Temperature
80 – 90
Blow Molding
°C
Die Temperature
175 – 215
Blow Molding
°C
Middle Barrel Temperature
175 – 215
Blow Molding
°C
MFI
0.35 – 0.4
ASTM D 1238, Load 2.16 kg
g/10min
Chemical Properties
Humidity content
<0.01
Blow Molding
%
Mechanical Properties
Tensile strength
25.05
Yield, Thickness 3.2 mm, 50 mm/min ; ASTM D638
MPa
Elongation at break-MD
262.7
Thickness 3.2 mm, 50 mm/min ; ASTM D638
%
Flexural strength
31.4
Yield, Thickness 6.4 mm,10 mm/min; ASTM D 790
MPa
Flexural modulus-MD
836.02
Thickness 6.4 mm, 10 mm/min; ASTM D 790
MPa