ABS SH610A
ABS SH610A is a general purpose high impact acrylonitrile butadiene styrene (ABS) grade.It is suitable for processing through extrusion.
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
Applications
Packaging > Industrial - Bags Automotive >interior
Advantages
high impact high fluidity high gloss high paintability general purpose
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Appearance Properties
Physical state
قرص
Physical Properties
Specific Gravity
1.04
ASTM D792
Shrinkage
0.4 – 0.7
ASTM D955;(Flow), 3.2mm
%
Melting range
200 – 250
اکستروژن
°C
Processing Properties
MFI
1
ASTM D1238;230℃/3.8kg
g/10min
Drying Temperature
70 – 80
اکستروژن
°C
Dry Time
180 – 240
اکستروژن
min
Die Temperature
200 – 250
اکستروژن
°C
Processing Temperature
180 – 210
Extrusion Molding;Barrel Temperature;Zone 1
°C
Processing Temperature
190 – 230
Extrusion Molding;Barrel Temperature;Zone 2
°C
Processing Temperature
200 – 250
Extrusion Molding;Barrel Temperature;Zone 3
°C
Processing Temperature
200 – 250
Extrusion Molding;Barrel Temperature;Zone 4
°C
Mechanical Properties
Tensile Stress at yield-MD
42.17
ASTM D638;50mm/min;3.2mm
MPa
Elongation at yield
>5
ASTM D638;50mm/min;3.2mm
%
Elongation at break-MD
35
ASTM D638;50mm/min;3.2mm
%
Flexural strength
63.74
ASTM D790;15mm/min;3.2mm
MPa
Flexural modulus-MD
1,961
ASTM D790;15mm/min;3.2mm
MPa
Izod impact strength (notched)
421.7
ASTM D256;23℃;6.4mm
J/m
Rockwell Hardness
97
ASTM D785;R-Scale
Izod impact strength (notched)
490.3
ASTM D256;23℃;3.2mm
J/m
Thermal Properties
Heat Deflection temperature
87
ASTM D648;6.4mm;(Unannealed);18.6kg
°C
Vicat softening temperature
94
ASTM D1525;5kg, 50℃/h
°C
Flameability
HB
UL94
Heat Deflection temperature
92
ASTM D648;6.4mm;(Unannealed);4.6kg
°C
Chemical Properties
Humidity content
<0.01