About us
|
Contact us
En
|
Fa
Login | Sign up
|
…
Coatings
Polyurethanes
Phenolics & Isocyanates
Engineering Plastics
General Plastics
Elastomers
Detergents
Additives
Pigments
Solvents
Silicones & Waxes
+98 21 91006091
Search products
LG Chemical HIPS 406AF PS, Flame Retardant | Metasan
Home
/
Products
/
PS GPPS
/ LG Chemical HIPS 406AF PS, Flame Retardant
LG Chemical HIPS 406AF PS, Flame Retardant
PS, Flame Retardant.
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
Applications
Parts of Printer or Copier
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Processing Properties
Linear Mold Shrinkage
0.004 – 0.008
Thickness 3.2 mm, ASTM D955
cm/cm
MFI
11
Temperature 200 °C, Load 5 kg, ASTM D 1238
g/10min
Dry Time
180 – 240
injection molding
min
Drying Temperature
60 – 70
injection molding
°C
Mold Temperature
40 – 60
injection molding
°C
Middle Barrel Temperature
190 – 200
injection molding
°C
Physical Properties
Specific Gravity
1.1
ASTM D792
Melting range
200 – 230
injection molding
°C
Chemical Properties
Humidity content
<0.01
injection molding
%
Mechanical Properties
Elongation at yield
>5
Thickness 3.2 mm, 50 mm/min ; ASTM D638
%
Tensile strength
32.3
Yield, Thickness 3.2 mm, 50 mm/min ; ASTM D638
MPa
Elongation at break-MD
50
Thickness 3.2 mm, 50 mm/min ; ASTM D638
%
Flexural strength
51.9
Yield, Thickness 3.2 mm, 15 mm/min; ASTM D 790
MPa
Flexural modulus-MD
2,451.6
Thickness 3.2 mm, 15 mm/min; ASTM D 790
MPa
Rockwell Hardness
103
ASTM D 785
Thermal Properties
Heat Deflection temperature
85
Unannealed; ASTM D648, 0.46 MPa (66 psi)
°C
Vicat softening temperature
85
50°C/h; ASTM D 1525, Load 5 kg
°C
UL RTI
50
Thickness 1.5,2.5,3 mm, Electrical
°C
Flameability
V-2
Thickness 1.5,2.5,3 mm
UL RTI
50
Thickness 1.5,2.5,3 mm, Mechanical with Impact
°C
UL RTI
50
Thickness 1.5,2.5,3 mm, Mechanical without Impact
°C