LG Chemical HIPS 403AF PS, Flame Retardant | Metasan
Home
/
Products
/
PS GPPS
/ LG Chemical HIPS 403AF PS, Flame Retardant
LG Chemical HIPS 403AF PS, Flame Retardant
PS, Flame Retardant.
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
Applications
Electric Parts Requiring Flame Retardancy
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Processing Properties
Linear Mold Shrinkage
0.004 – 0.008
Thickness 3.2 mm, ASTM D955
cm/cm
MFI
11
Temperature 200 °C, Load 5 kg, ASTM D 1238
g/10min
Dry Time
180 – 240
injection molding
min
Drying Temperature
60 – 70
injection molding
°C
Mold Temperature
40 – 60
injection molding
°C
Middle Barrel Temperature
190 – 200
injection molding
°C
Physical Properties
Specific Gravity
1.06
ASTM D792
Melting range
200 – 230
injection molding
°C
Chemical Properties
Humidity content
<0.01
injection molding
%
Mechanical Properties
Elongation at yield
>5
Thickness 3.2 mm, 50 mm/min ; ASTM D638
%
Tensile strength
24.5
Yield, Thickness 3.2 mm, 50 mm/min ; ASTM D638
MPa
Elongation at break-MD
60
Thickness 3.2 mm, 50 mm/min ; ASTM D638
%
Flexural strength
41.1
Yield, Thickness 3.2 mm, 15 mm/min; ASTM D 790
MPa
Flexural modulus-MD
2,255.5
Thickness 3.2 mm, 15 mm/min; ASTM D 790
MPa
Rockwell Hardness
97
ASTM D 785
Electrical Properties
Hot Wire Ignition
7 – 15
Thickness 1.5- mm, HWI
s
HAI)High Amp Arc Ignition)
>120
Thickness 1.5,3 mm, HAI
arcs
Arc Resistance
120 – 180
ASTM D 495
s
Comparative Tracking Index
400 – 600
V
Hot Wire Ignition
15 – 30
Thickness 3- mm, HWI
s
Thermal Properties
Heat Deflection temperature
77
Thickness 6.4 mm, 1.8 MPa (264 psi),Unannealed; ASTM D648
°C
Vicat softening temperature
83
Load 5 kg, 50°C/h; ASTM D 1525
°C
UL RTI
50
Thickness 1.6,3 mm, Electrical
°C
Flameability
V-2
Thickness 1.6,3.2 mm, UL94
UL RTI
50
Thickness 1.6,3 mm, Mechanical with Impact
°C
UL RTI
50
Thickness 1.6,3 mm, Mechanical without Impact
°C