LG Chemical LUPOL HF3308C PP+MF30%, High Impact | Metasan
Home
/
Products
/
Polypropylene
/ LG Chemical LUPOL HF3308C PP+MF30%, High Impact
LG Chemical LUPOL HF3308C PP+MF30%, High Impact
Polypropylene with 30% Mineral Filler. Used in Electrical & Electronic and Automotive Interior Parts.
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
Applications
Electrical, Electronic Automotive Interior Parts
Advantages
High Impact Good Weatherability
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Mechanical Properties
Flexural modulus-MD
2,840
30mm/min; ASTM D790@Thickness 6.40 mm
MPa
Izod impact strength (notched)
>52
ASTM D256@Thickness 6.4 mm, Temperature 23.0 °C
J/m
Tensile Stress at yield-MD
24.5
50mm/min; ASTM D638@Thickness 3.20 mm
MPa
Flexural strength
40.7
Yield;30mm/min; ASTM D790@Thickness 6.40 mm
MPa
Elongation at break-MD
50
50mm/min; ASTM D638@Thickness 3.20 mm
%
Thermal Properties
Heat Deflection temperature
135
Unannealed; ASTM D648@Thickness 3.20 mm;at 0.46 MPa
°C
UL RTI
120
Electrical@Thickness >=1.50 mm
°C
Flameability
HB
@Thickness >=1.50 mm
UL RTI
120
Electrical@Thickness >=3.00 mm
°C
Flameability
HB
@Thickness >=3.00 mm
UL RTI
120
Mechanical with Impact@Thickness >=1.50 mm
°C
UL RTI
120
Mechanical with Impact@Thickness >=3.00 mm
°C
UL RTI
120
Mechanical without Impact@Thickness >=1.50 mm
°C
UL RTI
120
Mechanical without Impact@Thickness >=3.00 mm
°C
Physical Properties
Melting range
200 – 230
قالب گیری تزریقی
°C
Specific Gravity
1.3
ASTM D792
Processing Properties
Mold Temperature
40 – 60
قالب گیری تزریقی
°C
Dry Time
180 – 240
قالب گیری تزریقی
min
Middle Barrel Temperature
200 – 230
قالب گیری تزریقی
°C
Drying Temperature
70 – 80
قالب گیری تزریقی
°C
MFI
12
ASTM D1238@Load 2.16 kg;Temperature 230 °C
g/10min
Linear Mold Shrinkage
0.007 – 0.009
ASTM D955;Flow@Thickness 3.20 mm
cm/cm
Chemical Properties
Humidity content
<0.010