LG Chemical LUPOL GP3102Y PP+MF10%, High Impact, High Flow | Metasan
Home
/
Products
/
Polypropylene
/ LG Chemical LUPOL GP3102Y PP+MF10%, High Impact, High Flow
LG Chemical LUPOL GP3102Y PP+MF10%, High Impact, High Flow
Polypropylene with 10% Mineral Filler,General Purpose. Used in Electrical & Electronic, Automotive Parts.
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
Applications
Electrical & Electronic Automotive Parts
Advantages
High Impact High Flow
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Mechanical Properties
Tensile Stress at yield-MD
26.5
50mm/min; ASTM D638@Thickness 3.20 mm
MPa
Izod impact strength (notched)
>88
ASTM D256@Thickness 6.4 mm, Temperature 23.0 °C
J/m
Flexural modulus-MD
1,570
1.3mm/min; ASTM D790@Thickness 6.40 mm
MPa
Flexural strength
35.3
Yield;1.3mm/min; ASTM D790@Thickness 6.40 mm
MPa
Elongation at break-MD
60
50mm/min; ASTM D638@Thickness 3.20 mm
%
Processing Properties
Linear Mold Shrinkage
0.009 – 0.014
ASTM D955;Flow@Thickness 3.20 mm
cm/cm
MFI
13
ASTM D1238@Load 2.16 kg;Temperature 230 °C
g/10min
Drying Temperature
70 – 80
قالب گیری تزریقی
°C
Middle Barrel Temperature
200 – 230
قالب گیری تزریقی
°C
Dry Time
180 – 240
قالب گیری تزریقی
min
Mold Temperature
40 – 60
قالب گیری تزریقی
°C
Chemical Properties
Humidity content
<0.010
قالب گیری تزریقی
%
Physical Properties
Melting range
200 – 230
قالب گیری تزریقی
°C
Specific Gravity
1
ASTM D792
Thermal Properties
Heat Deflection temperature
130
Unannealed; ASTM D648@Thickness 3.20 mm;at 0.46 MPa
°C