LG Chemical LUPOL TE5007B PP+Rubber, High Impact | Metasan
Home
/
Products
/
Polypropylene
/ LG Chemical LUPOL TE5007B PP+Rubber, High Impact
LG Chemical LUPOL TE5007B PP+Rubber, High Impact
Polypropylene with Rubber. Used in Automotive Exterior Parts.
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
Applications
Automotive Exterior Parts (Bumper Fascia, Rear Bumper Step)
Advantages
Low Density High Impact Good Weatherability
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Mechanical Properties
Tensile Stress at yield-MD
14.7
50mm/min; ASTM D638@Thickness 3.20 mm
MPa
Izod impact strength (notched)
NB
ASTM D256@Thickness 6.4 mm, Temperature 23.0 °C
J/m
Flexural modulus-MD
735
10mm/min; ASTM D790@Thickness 6.40 mm
MPa
Flexural strength
39.2
Yield;10mm/min; ASTM D790@Thickness 6.40 mm
MPa
Elongation at break-MD
400
50mm/min; ASTM D638@Thickness 3.20 mm
%
Izod impact strength (notched)
>98
ASTM D256@Thickness 6.4 mm, Temperature -10.0 °C
J/m
Processing Properties
Linear Mold Shrinkage
0.009 – 0.01
ASTM D955;Flow@Thickness 3.20 mm
cm/cm
MFI
20
ASTM D1238@Load 2.16 kg;Temperature 230 °C
g/10min
Drying Temperature
70 – 80
قالب گیری تزریقی
°C
Middle Barrel Temperature
200 – 230
قالب گیری تزریقی
°C
Dry Time
180 – 240
قالب گیری تزریقی
min
Mold Temperature
40 – 60
قالب گیری تزریقی
°C
Chemical Properties
Humidity content
<0.010
قالب گیری تزریقی
%
Physical Properties
Melting range
200 – 230
قالب گیری تزریقی
°C
Specific Gravity
0.9
ASTM D792
Thermal Properties
Heat Deflection temperature
85
Unannealed; ASTM D648@Thickness 6.40 mm;at 0.46 MPa
°C