LG Chemical LUPOL HG3200SK2 PP+MF20%, High Gloss | Metasan
Home
/
Products
/
Polypropylene
/ LG Chemical LUPOL HG3200SK2 PP+MF20%, High Gloss
LG Chemical LUPOL HG3200SK2 PP+MF20%, High Gloss
Polypropylene with 20% Mineral Filler. Used in Electrical & Electronic Parts.
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
Applications
Electrical & Electronic Parts
Advantages
High Gloss
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Mechanical Properties
Flexural modulus-MD
1,960
10mm/min; ASTM D790@Thickness 6.40 mm
MPa
Izod impact strength (notched)
>39
ASTM D256@Thickness 6.4 mm, Temperature 23.0 °C
J/m
Tensile Stress at yield-MD
34.3
50mm/min; ASTM D638@Thickness 3.20 mm
MPa
Flexural strength
44.1
Yield;10mm/min; ASTM D790@Thickness 6.40 mm
MPa
Elongation at break-MD
20
50mm/min; ASTM D638@Thickness 3.20 mm
%
Thermal Properties
Heat Deflection temperature
125
Unannealed; ASTM D648@Thickness 3.20 mm;at 0.46 MPa
°C
UL RTI
120
Electrical@Thickness >=1.50 mm
°C
Flameability
HB
@Thickness >=1.50 mm
UL RTI
120
Electrical@Thickness >=3.00 mm
°C
Flameability
HB
@Thickness >=3.00 mm
UL RTI
120
Mechanical with Impact@Thickness >=1.50 mm
°C
UL RTI
120
Mechanical with Impact@Thickness >=3.00 mm
°C
UL RTI
120
Mechanical without Impact@Thickness >=1.50 mm
°C
UL RTI
120
Mechanical without Impact@Thickness >=3.00 mm
°C
Physical Properties
Melting range
200 – 230
قالب گیری تزریقی
°C
Specific Gravity
1.05
ASTM D792
Processing Properties
Mold Temperature
40 – 60
قالب گیری تزریقی
°C
Dry Time
180 – 240
قالب گیری تزریقی
min
Middle Barrel Temperature
200 – 230
قالب گیری تزریقی
°C
Drying Temperature
70 – 80
قالب گیری تزریقی
°C
MFI
22
ASTM D1238@Load 2.16 kg;Temperature 230 °C
g/10min
Linear Mold Shrinkage
0.014 – 0.018
ASTM D955;Flow@Thickness 3.20 mm
cm/cm
Chemical Properties
Humidity content
<0.010
قالب گیری تزریقی
%
Electrical Properties
Hot Wire Ignition
15 – 30
@Thickness >=1.50 mm
s
HAI)High Amp Arc Ignition)
>120
@Thickness 1.50 mm
arcs
Hot Wire Ignition
15 – 30
@Thickness >=3.00 mm
s
HAI)High Amp Arc Ignition)
>120
@Thickness 3.00 mm
arcs