LG Chemical LUPOL HF5150H PP+MF15%, High Flow
Polypropylene with 15% Mineral Filler. Used in Automotive Interior Parts.
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
Applications
Automotive Interior Parts
Advantages
High Flow
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Mechanical Properties
Elongation at break-MD
10
50mm/min; ASTM D638@Thickness 3.20 mm
%
Flexural strength
36.3
Yield;30mm/min; ASTM D790@Thickness 6.40 mm
MPa
Tensile Stress at yield-MD
25.5
50mm/min; ASTM D638@Thickness 3.20 mm
MPa
Izod impact strength (notched)
>39
ASTM D256@Thickness 6.4 mm, Temperature 23.0 °C
J/m
Flexural modulus-MD
1,770
30mm/min; ASTM D790@Thickness 6.40 mm
MPa
Izod impact strength (notched)
>19
ASTM D256@Thickness 6.4 mm, Temperature -10.0 °C
J/m
Physical Properties
Specific Gravity
1.01
ASTM D792
Melting range
200 – 230
قالب گیری تزریقی
°C
Processing Properties
Linear Mold Shrinkage
0.011 – 0.015
ASTM D955;Flow@Thickness 3.20 mm
cm/cm
MFI
100
ASTM D1238@Load 2.16 kg;Temperature 230 °C
g/10min
Drying Temperature
70 – 80
قالب گیری تزریقی
°C
Middle Barrel Temperature
200 – 230
قالب گیری تزریقی
°C
Dry Time
180 – 240
قالب گیری تزریقی
min
Mold Temperature
40 – 60
قالب گیری تزریقی
°C
Chemical Properties
Humidity content
<0.010
قالب گیری تزریقی
%
Thermal Properties
Heat Deflection temperature
130
Unannealed; ASTM D648@Thickness 6.40 mm;at 0.46 MPa
°C