LG Chemical LUPOL LW4405 PP+GF/MF40% | Metasan
Home
/
Products
/
Polypropylene
/
Glass fiber
/ LG Chemical LUPOL LW4405 PP+GF/MF40%
LG Chemical LUPOL LW4405 PP+GF/MF40%
Polypropylene with 40% Glass Fiber and Mineral Fillers. Used in Electrical, Electronic and Automotive Parts.
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
Applications
Electrical, Electronic Automotive Parts
Advantages
Low Warpage
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Thermal Properties
Heat Deflection temperature
155
Unannealed; ASTM D648@Thickness 3.20 mm;at 0.46 MPa
°C
UL RTI
65
Electrical@Thickness >=1.50mm
°C
Flameability
HB
Thickness >=1.50 mm@
UL RTI
65
Mechanical with Impact@Thickness >=1.50mm
°C
UL RTI
65
Mechanical without Impact@Thickness >=1.50mm
°C
Mechanical Properties
Izod impact strength (notched)
>83
ASTM D256@Thickness 6.4 mm, Temperature 23.0 °C
J/m
Tensile Stress at yield-MD
85.3
5mm/min; ASTM D638@Thickness 3.20 mm
MPa
Flexural strength
127
Yield;1.3mm/min; ASTM D790@Thickness 6.40 mm
MPa
Elongation at break-MD
>10
5mm/min; ASTM D638@Thickness 3.20 mm
%
Flexural modulus-MD
7,060
1.3mm/min; ASTM D790@Thickness 6.40 mm
MPa
Physical Properties
Melting range
200 – 230
قالب گیری تزریقی
°C
Specific Gravity
1.2
ASTM D792
Processing Properties
Mold Temperature
40 – 60
قالب گیری تزریقی
°C
Dry Time
180 – 240
قالب گیری تزریقی
min
Middle Barrel Temperature
200 – 230
قالب گیری تزریقی
°C
Drying Temperature
70 – 80
قالب گیری تزریقی
°C
MFI
3
ASTM D1238@Load 2.16 kg;Temperature 230 °C
g/10min
Linear Mold Shrinkage
0.002 – 0.004
ASTM D955;Flow@Thickness 3.20 mm
cm/cm
Chemical Properties
Humidity content
<0.010
قالب گیری تزریقی
%