LG Chemical LUPOL GP3400S PP+MF40% | Metasan
Home
/
Products
/
Polypropylene
/ LG Chemical LUPOL GP3400S PP+MF40%
LG Chemical LUPOL GP3400S PP+MF40%
Polypropylene with 40% Mineral Filler,General Purpose. Used in Electrical & Electronic, Automotive Interior Parts.
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
Applications
Electrical & Electronic Automotive Interior Parts
Advantages
Low Warpage
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Mechanical Properties
Elongation at break-MD
5
5mm/min; ASTM D638@Thickness 3.20 mm
%
Flexural strength
51
Yield;1.3mm/min; ASTM D790@Thickness 6.40 mm
MPa
Tensile Stress at yield-MD
33.3
5mm/min; ASTM D638@Thickness 3.20 mm
MPa
Izod impact strength (notched)
>24
ASTM D256@Thickness 6.4 mm, Temperature 23.0 °C
J/m
Flexural modulus-MD
6,670
1.3mm/min; ASTM D790@Thickness 6.40 mm
MPa
Physical Properties
Specific Gravity
1.2
ASTM D792
Melting range
200 – 230
قالب گیری تزریقی
°C
Processing Properties
Linear Mold Shrinkage
0.007 – 0.01
ASTM D955;Flow@Thickness 3.20 mm
cm/cm
MFI
7
ASTM D1238@Load 2.16 kg;Temperature 230 °C
g/10min
Drying Temperature
70 – 80
قالب گیری تزریقی
°C
Middle Barrel Temperature
200 – 230
قالب گیری تزریقی
°C
Dry Time
180 – 240
قالب گیری تزریقی
min
Mold Temperature
40 – 60
قالب گیری تزریقی
°C
Chemical Properties
Humidity content
<0.010
قالب گیری تزریقی
%
Thermal Properties
Heat Deflection temperature
120
Unannealed; ASTM D648@Thickness 3.20 mm;at 0.46 MPa
°C