LG Chemical LUPOL GP3302 PP+MF30% | Metasan
Home
/
Products
/
Polypropylene
/ LG Chemical LUPOL GP3302 PP+MF30%
LG Chemical LUPOL GP3302 PP+MF30%
Polypropylene with 30% Mineral Filler,General Purpose. Used in Electrical & Electronic, Automotive Interior Parts.
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
Applications
Electrical & Electronic Automotive Interior Parts
Advantages
Good Weatherability
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Mechanical Properties
Elongation at break-MD
30
50mm/min; ASTM D638@Thickness 3.20 mm
%
Flexural strength
40.2
Yield;30mm/min; ASTM D790@Thickness 6.40 mm
MPa
Tensile Stress at yield-MD
29.4
50mm/min; ASTM D638@Thickness 3.20 mm
MPa
Izod impact strength (notched)
>44
ASTM D256@Thickness 6.4 mm, Temperature 23.0 °C
J/m
Flexural modulus-MD
3,140
30mm/min; ASTM D790@Thickness 6.40 mm
MPa
Physical Properties
Specific Gravity
1.14
ASTM D792
Melting range
200 – 230
قالب گیری تزریقی
°C
Processing Properties
Linear Mold Shrinkage
0.007 – 0.01
ASTM D955;Flow@Thickness 3.20 mm
cm/cm
MFI
10
ASTM D1238@Load 2.16 kg;Temperature 230 °C
g/10min
Drying Temperature
70 – 80
قالب گیری تزریقی
°C
Middle Barrel Temperature
200 – 230
قالب گیری تزریقی
°C
Dry Time
180 – 240
قالب گیری تزریقی
min
Mold Temperature
40 – 60
قالب گیری تزریقی
°C
Chemical Properties
Humidity content
<0.010
قالب گیری تزریقی
%
Thermal Properties
Heat Deflection temperature
137
Unannealed; ASTM D648@Thickness 3.20 mm;at 0.46 MPa
°C
UL RTI
65
Electrical@Thickness >=1.50mm
°C
Flameability
HB
@Thickness >=1.50 mm
UL RTI
65
Mechanical with Impact@Thickness >=1.50mm
°C
UL RTI
65
Mechanical without Impact@Thickness >=1.50mm
°C