LG Chemical LUPOL GP2100 PP+GF10% | Metasan
Home
/
Products
/
Polypropylene
/
Glass fiber
/ LG Chemical LUPOL GP2100 PP+GF10%
LG Chemical LUPOL GP2100 PP+GF10%
Polypropylene with 10% Glass Fiber, General Purpose. Used in Electrical & Electronic, Automotive Parts.
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
Applications
Electrical & Electronic Automotive Parts
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Mechanical Properties
Flexural modulus-MD
1,960
1.3mm/min; ASTM D790@Thickness 6.40 mm
MPa
Flexural strength
68.6
Yield; 1.3mm/min; ASTM D790@Thickness 6.40 mm
MPa
Elongation at break-MD
>10
50mm/min; ASTM D638@Thickness 3.20 mm
%
Izod impact strength (notched)
>49
ASTM D256@Thickness 6.4 mm, Temperature 23.0 °C
J/m
Tensile Stress at yield-MD
49
50mm/min; ASTM D638@Thickness 3.20 mm
MPa
Physical Properties
Specific Gravity
0.99
ASTM D792
Melting range
200 – 230
قالب گیری تزریقی
°C
Thermal Properties
Heat Deflection temperature
140
Unannealed; ASTM D648@Thickness 3.20 mm;at 0.46 MPa
°C
Processing Properties
Mold Temperature
40 – 60
قالب گیری تزریقی
°C
Dry Time
180 – 240
قالب گیری تزریقی
min
Middle Barrel Temperature
200 – 230
قالب گیری تزریقی
°C
Drying Temperature
70 – 80
قالب گیری تزریقی
°C
MFI
15
ASTM D1238@Temperature 230 °C
g/10min
Linear Mold Shrinkage
0.004 – 0.006
ASTM D955;Flow@Thickness 3.20 mm
cm/cm
MFI
15
ASTM D1238@Load 2.16 kg
g/10min
Chemical Properties
Humidity content
<0.010
قالب گیری تزریقی
%