LG Chemical LUPOL EI5002L PP | Metasan
Home
/
Products
/
Polypropylene
/ LG Chemical LUPOL EI5002L PP
LG Chemical LUPOL EI5002L PP
Polypropylene, General Purpose. Used in Automotive Interior Parts.
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
Applications
Automotive Interior Parts
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Mechanical Properties
Flexural modulus-MD
1,270
30mm/min; ASTM D790@Thickness 6.40 mm
MPa
Tensile Stress at yield-MD
25
50mm/min; ASTM D638@Thickness 3.20 mm
MPa
Flexural strength
34.3
Yield; 30mm/min; ASTM D790@Thickness 6.40 mm
MPa
Elongation at break-MD
80
50mm/min; ASTM D638@Thickness 3.20 mm
%
Izod impact strength (notched)
>49
ASTM D256@Thickness 6.4 mm, Temperature -10.0°C
J/m
Izod impact strength (notched)
>196
ASTM D256@Thickness 6.4 mm, Temperature 23.0 °C
J/m
Thermal Properties
Heat Deflection temperature
120
Unannealed; ASTM D648@Thickness 3.20 mm;at 0.46 MPa
°C
Processing Properties
Mold Temperature
40 – 60
قالب گیری تزریقی
°C
Dry Time
180 – 240
قالب گیری تزریقی
min
MFI
25
ASTM D1238@Temperature 230 °C
g/10min
Linear Mold Shrinkage
0.016 – 0.018
ASTM D955;Flow@Thickness 3.20 mm
cm/cm
Drying Temperature
70 – 80
قالب گیری تزریقی
°C
Middle Barrel Temperature
200 – 230
قالب گیری تزریقی
°C
MFI
25
ASTM D1238@Load 2.16 kg
g/10min
Physical Properties
Specific Gravity
0.91
ASTM D792
Melting range
200 – 230
قالب گیری تزریقی
°C
Chemical Properties
Humidity content
<0.01
قالب گیری تزریقی
%