Specifications
PropertyValueUnit
Thermal Properties
FlameabilityHBIEC 707@Thickness 1.60 mm
Thermal Expansion70ASTM E831 @Temperature 0.000 -50.0 °Cum/(m-°C)
Heat Deflection temperature109ISO 75; at 0.46 MPa°C
Vicat softening temperature119B50; ISO 306°C
Glass transition Temperature122IEC 10006°C
Heat Deflection temperature106ISO 75; at 1.8 MPa°C
Physical Properties
Density1.19ISO 1183g/mL
Moisture absorption0.6Humidity Absorption (23°C, 50%); ISO62; at Equilibrium%
Melting range220 – 250°C
Mechanical Properties
Tensile Stress at break-MD805mm/min; ISO 527MPa
Elongation at break-MD3.55mm/min; ISO 527%
Tensile modulus-MD3,6001mm/min; ISO 527MPa
(Charpy Impact Strength(unnotched20ISO 179@Temperature 23.0 °CkJ/m2
Optical Properties
Transmittance90Transmission Factor; DIN 5036;Visible%
Chemical Properties
Water absorption2.2Water Absorption in Water; ISO 62; at Saturation%
Processing Properties
MFI1.428ISO 1133@Load 3.80 kg,Temperature 230 °Cg/10min
Processing Temperature220 – 250Cylinder Temperature°C
Mold Temperature60 – 90°C
Drying Temperature<109Predrying°C
Dry Time120 – 180Desiccant-type driermin
Appearance Properties
Refractive index1.51ISO 489