Specifications
PropertyValueUnit
Processing Properties
Processing Temperature230 – 240Cylinder/Barrel Temperature°C
MFI1.61ISO 1133@Load 3.80 kg,Temperature 230 °Cg/10min
Mold Temperature50 – 70°C
Drying Temperature<90.0Predrying°C
Dry Time120 – 180Desiccant-type driermin
Appearance Properties
Refractive index1.49ISO 489
Thermal Properties
Vicat softening temperature98B50; ISO 306°C
FlameabilityHBIEC 707@Thickness 1.60 mm
Heat Deflection temperature91ISO 75; at 1.8 MPa°C
Thermal Expansion110ASTM E831 @Temperature 0.000 -50.0 °Cum/(m-°C)
Heat Deflection temperature96ISO 75; at 0.46 MPa°C
Mechanical Properties
(Charpy Impact Strength(unnotched55ISO 179@Temperature 23.0 °CkJ/m2
Elongation at yield4.550mm/min; ISO 527%
Tensile modulus-MD2,0001mm/min; ISO 527MPa
Elongation at break-MD27ISO 527%
Tensile Stress at yield-MD5150mm/min; ISO 527MPa
Chemical Properties
Water absorption1.7Immersion; ISO 62;at Saturation%
Physical Properties
Moisture absorption0.523°C, 50%; ISO 62; at Equilibrium%
Density1.15ISO 1183g/mL
Melting range230 – 240°C
Optical Properties
Transmittance90Transmission Factor; DIN 5036;Visible%