Specifications
PropertyValueUnit
Physical Properties
Melting range230 – 240°C
Moisture absorption0.423°C, 50%; ISO 62; at Equilibrium%
Density1.12ISO 1183g/mL
Processing Properties
Processing Temperature230 – 240Cylinder/Barrel Temperature°C
MFI0.112ISO 1133@Load 3.80 kg,Temperature 230 °Cg/10min
Mold Temperature50 – 70°C
Drying Temperature<70.0Predrying°C
Dry Time120 – 180Desiccant-type driermin
Appearance Properties
Refractive index1.49ISO 489
Thermal Properties
FlameabilityHBIEC 707@Thickness 1.60 mm
Heat Deflection temperature70ISO 75; at 1.8 MPa°C
Vicat softening temperature75B50; ISO 306°C
Thermal Expansion150ASTM E831 @Temperature 0.000 -50.0 °Cum/(m-°C)
Glass transition Temperature115ISO 11357°C
Heat Deflection temperature73ISO 75; at 0.46 MPa°C
Mechanical Properties
(Charpy Impact Strength(unnotchedNBISO 179@Temperature 23.0 °CkJ/m2
Elongation at yield550mm/min; ISO 527%
Tensile modulus-MD9501mm/min; ISO 527MPa
Elongation at break-MD>50ISO 527%
Tensile Stress at yield-MD2550mm/min; ISO 527MPa
Charpy Impact Strength (notched)13ISO 179kJ/m2
Chemical Properties
Water absorption1.2Immersion; ISO 62;at Saturation%
Optical Properties
Transmittance89Transmission Factor; DIN 5036;Visible%