Specifications
PropertyValueUnit
Thermal Properties
FlameabilityHBIEC 707@Thickness 1.60 mm
Glass transition Temperature108ISO 11357°C
Thermal Expansion80ASTM E831 @Temperature 0.000 -50.0 °Cum/(m-°C)
Vicat softening temperature102B50; ISO 306°C
Physical Properties
Density1.18ISO 1183g/mL
Moisture absorption0.623°C, 50%; ISO 62; at Equilibrium%
Melting range220 – 260°C
Mechanical Properties
Tensile Stress at yield-MD6850mm/min; ISO 527MPa
Elongation at break-MD17ISO 527%
Tensile modulus-MD2,9001mm/min; ISO 527MPa
Elongation at yield4.550mm/min; ISO 527%
(Charpy Impact Strength(unnotched25ISO 179@Temperature 23.0 °CkJ/m2
Optical Properties
Transmittance92Transmission Factor; DIN 5036;Visible%
Chemical Properties
Water absorption2Immersion; ISO 62;at Saturation%
Processing Properties
MFI1.298ISO 1133@Load 3.80 kg,Temperature 230 °Cg/10min
Processing Temperature220 – 260Barrel Temperature°C
Die Temperature220 – 260°C
Drying Temperature<90.0Predrying°C
Dry Time120 – 180Desiccant-type driermin
Appearance Properties
Refractive index1.49ISO 489