Specifications
PropertyValueUnit
Processing Properties
Die Temperature220 – 260°C
Processing Temperature220 – 260Barrel Temperature°C
MFI0.819ISO 1133@Load 3.80 kg,Temperature 230 °Cg/10min
Drying Temperature<90.0Predrying°C
Dry Time120 – 180Desiccant-type driermin
Thermal Properties
Vicat softening temperature100B50; ISO 306°C
Thermal Expansion90ASTM E831 @Temperature 0.000 -50.0 °Cum/(m-°C)
FlameabilityHBIEC 707@Thickness 1.60 mm
Mechanical Properties
(Charpy Impact Strength(unnotched55ISO 179@Temperature 23.0 °CkJ/m2
Elongation at yield550mm/min; ISO 527%
Elongation at break-MD28ISO 527%
Tensile modulus-MD2,5001mm/min; ISO 527MPa
Tensile Stress at yield-MD6350mm/min; ISO 527MPa
Physical Properties
Moisture absorption0.523°C, 50%; ISO 62; at Equilibrium%
Density1.17ISO 1183g/mL
Melting range220 – 260°C
Chemical Properties
Water absorption1.9Immersion; ISO 62;at Saturation%
Optical Properties
Transmittance92Transmission Factor; DIN 5036;Visible%
Appearance Properties
Refractive index1.49ISO 489