Specifications
PropertyValueUnit
Appearance Properties
Refractive index1.49ISO 489
Thermal Properties
Thermal Expansion110ASTM E831 @Temperature 0.000 -50.0 °Cum/(m-°C)
Vicat softening temperature97B50; ISO 306°C
FlameabilityHBIEC 707@Thickness 1.60 mm
Mechanical Properties
Tensile modulus-MD2,0001mm/min; ISO 527MPa
Elongation at break-MD48ISO 527%
Tensile Stress at yield-MD4750mm/min; ISO 527MPa
Elongation at yield5.550mm/min; ISO 527%
(Charpy Impact Strength(unnotched80ISO 179@Temperature 23.0 °CkJ/m2
Processing Properties
Die Temperature220 – 260°C
Drying Temperature<85.0Predrying°C
Dry Time120 – 180Desiccant-type driermin
MFI0.464ISO 1133@Load 3.80 kg,Temperature 230 °Cg/10min
Processing Temperature220 – 260Barrel Temperature°C
Physical Properties
Density1.16ISO 1183g/mL
Moisture absorption0.523°C, 50%; ISO 62; at Equilibrium%
Melting range220 – 260°C
Optical Properties
Transmittance91Transmission Factor; DIN 5036;Visible%
Chemical Properties
Water absorption1.8Immersion; ISO 62;at Saturation%