Specifications
PropertyValueUnit
Thermal Properties
Glass transition Temperature108IEC 10006°C
Thermal Expansion80ASTM E831 @Temperature 0.000 -50.0 °Cum/(m-°C)
Heat Deflection temperature99ISO 75; at 0.46 MPa°C
Vicat softening temperature102B50; ISO 306°C
FlameabilityHBIEC 707@Thickness 1.60 mm
Heat Deflection temperature95ISO 75; at 1.8 MPa°C
Physical Properties
Density1.18ISO 1183g/mL
Moisture absorption0.623°C, 50%; ISO 62; at Equilibrium%
Melting range220 – 260°C
Mechanical Properties
Tensile Stress at yield-MD7150mm/min; ISO 527MPa
Elongation at break-MD19ISO 527%
Tensile modulus-MD2,8001mm/min; ISO 527MPa
Elongation at yield4.550mm/min; ISO 527%
(Charpy Impact Strength(unnotched25ISO 179@Temperature 23.0 °CkJ/m2
Optical Properties
Haze<1.5ASTM D1003%
Transmittance92Transmission Factor; DIN 5036;Visible%
Chemical Properties
Water absorption2Immersion; ISO 62;at Saturation%
Processing Properties
MFI5.31ISO 1133@Load 3.80 kg,Temperature 230 °Cg/10min
Processing Temperature220 – 260Barrel Temperature°C
Mold Temperature50 – 70°C
Drying Temperature<90.0Predrying°C
Dry Time120 – 180Desiccant-type driermin
Appearance Properties
Refractive index1.49ISO 489