Mechanical Properties
Strain at break-MD>150Tensile test of filaments (aspect ratio 1:3, av. filament diam. ca. 0.37 mm, at temperature 23.0 ); ISO 527-1/2; After conditioning (3h / 180°C)%
Tensile modulus-MD3,700ISO 527-1/2MPa
Tensile Stress at break-MD100ISO 527-1/2MPa
Strain at break-MD3ISO 527-1/2%
Tensile Stress at break-MD>300Tensile test of filaments (aspect ratio 1:3, av. filament diam. ca. 0.37 mm, at temperature 23.0 ); ISO 527-1/2; After extrusionMPa
Strain at break-MD>150Tensile test of filaments (aspect ratio 1:3, av. filament diam. ca. 0.37 mm, at temperature 23.0 ); ISO 527-1/2; After extrusion%
Tensile Stress at break-MD>300Tensile test of filaments (aspect ratio 1:3, av. filament diam. ca. 0.37 mm, at temperature 23.0 ); ISO 527-1/2; After conditioning (3h / 180°C)MPa