Vestamid® L-CD22-M Black Flame Retardant Nylon 12
Description: Graphite filled, medium-viscosity, heat-stabilized. Applications: Dust caps for ignition distributor, parts with improved frictional performance. Information provided by degussa.
Packaging
Price unavailable
Unit price
Price unavailable
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
Applications
Dust caps for ignition distributor
parts with improved frictional performance
Advantages
Heat-stabilized, Flame Retardant
Specifications
Property
Value
Unit
Electrical Properties
Dielectric Constant
7
IEC 60250@Frequency 100 Hz
Volume resistance
1,000,000,000,000
IEC 60093
ohm-cm
Comparative Tracking Index
200
Test Solution A, 50 drops; IEC 60112
V
Dissipation Factor
0.033
IEC 60250@Frequency 1e+6 Hz
Dielectric Strength
7
K20/P50; IEC 60243-1
kV/mm
Dielectric Constant
5
IEC 60250@Frequency 1e+6 Hz
Dissipation Factor
0.058
IEC 60250@Frequency 100 Hz
Comparative Tracking Index
175
Test Solution A, 100 drops; IEC 60112
V
Thermal Properties
Vicat softening temperature
160
50N; ISO 306
degC
Heat Deflection temperature
80
ISO 75;at 1.8 MPa
degC
Flameability
HB
@Thickness 3.20 mm
Thermal Expansion
80
45x15x10 mm; ISO 11359 @Temperature 23.0 -55.0 °C
um/(m-degC)
Heat Deflection temperature
160
ISO 75;at 0.46 MPa
degC
Vicat softening temperature
175
10N; ISO 306
degC
Flameability
HB
@Thickness 1.60 mm
Mechanical Properties
Charpy Impact Strength (notched)
6
ISO 179/1eA@Temperature -30.0 °C
kJ/m2
Tensile modulus-MD
2,800
ISO 527-1/2
MPa
(Charpy Impact Strength(unnotched
34
ISO 179/1eU@Temperature -30.0 °C
kJ/m2
Tensile Stress at yield-MD
45
ISO 527-1/2
MPa
Elongation at yield
5
ISO 527-1/2
%
Elongation at break-MD
6
ISO 527-1/2
%
Tensile Stress at break-MD
45
ISO 527-1/2
MPa
Charpy Impact Strength (notched)
6
ISO 179/1eA@Temperature 23.0 °C
kJ/m2
(Charpy Impact Strength(unnotched
34
ISO 179/1eU@Temperature 23.0 °C
kJ/m2
Physical Properties
Density
1.17
ISO 1183
g/mL
Melting point
178
Peak Temperature; ISO 3146, ISO11357
degC
Moisture absorption
0.5
ISO 62; at Equilibrium@Temperature 23.0 °C, 50% R.H.
%
Moisture absorption
0.5
ISO 62; at Equilibrium@Thickness 1.00 mm, 50% R.H
%
Processing Properties
Linear Mold Shrinkage
0.006
127x12.7x3.2 mm (processing cond.acc. To ISO 1874-2)
cm/cm
Linear Mold Shrinkage
0.009
127x12.7x3.2 mm (processing cond.acc. To ISO 1874-2); Transverse
cm/cm
Chemical Properties
Electrolytic Corrosion
A1 Step
IEC 60426
Water absorption
1.2
ISO 62; at Saturation@Thickness 1.00 mm
%