Rohacell® 110 IG Industrial Grade Polymethacrylimide (PMI) Foam

Description: ROHACELL® is produced by thermal expansion of a co-polymer sheet of methacrylic acid and methacrylonitrile. During the foaming process the copolymer sheet is converted to PMI- PolyMethacrylImide. Alcohol is used as a blowing agent,thus ROHACELL® contains no fluorinated carbon hydrates and is halogen free. Information provided by degussa.

Packaging

Price unavailable

Unit price

Price inquiry required

Producer

Delivery location-

Minimum order-

Order quantity

Additional Information

Applications: The fields of application for ROHACELL® IG are model building, vehicle construction and shipbuilding, as well as the manufacture of sports articles and X-ray tables.
Advantages: very homogeneous cell structure isotropic properties a closed-cell rigid foam plastic based on PMI (polymethacrylimide) does not contain any CFCs

Reviews

No reviews yet.

Specifications

PropertyValueUnit

Mechanical Properties

Flexural strength4.5DIN 53423, ISO 1209, ASTM D 790MPa

Tensile Stress at break-MD3.5DIN 53455, ISO 527-2, ASTM D 638MPa

Elongation at break-MD4.5DIN 53455, ISO 527-2, ASTM D 638%

Tensile modulus-MD160ISO 527-2, ASTM D 638MPa

Compressive Strength3DIN 53421, ISO 844, ASTM D 1621MPa

shear modulus50DIN 53294, ASTM C 273MPa

shear strength2.4DIN 53294, ASTM C 273MPa

Thermal Properties

Maximum Service Temperature180Heat Distortion Resistance; DIN 53424; Air°C

Physical Properties

Density0.11DIN 53420, ISO 845, ASTM D 1622g/mL

Rohacell® 110 IG Industrial Grade Polymethacrylimide (PMI) Foam

Additional Information

Reviews

Specifications

Rohacell® 110 IG Industrial Grade Polymethacrylimide (PMI) Foam

Additional Information

Reviews

Submit review

Specifications

Mechanical Properties

Thermal Properties

Physical Properties

Additional Information

Reviews

Specifications

Additional Information

Reviews

Submit review

Specifications

Mechanical Properties

Thermal Properties

Physical Properties