Specifications
PropertyValueUnit
Mechanical Properties
Izod impact strength (notched)80.1ASTM D256@Thickness 3.17 mm, Temperature 0.000 °CJ/m
Elongation at break-MD19ASTM D638%
Tensile Stress at yield-MD33.64ASTM D638MPa
Tensile modulus-MD1,530ASTM D638MPa
Rockwell Hardness44Rockwell L; ASTM D785
Elongation at yield4.7ASTM D638%
Izod impact strength (notched)74.7ASTM D256@Thickness 6.35 mm, Temperature 23.0 °CJ/m
Izod impact strength (notched)80.1ASTM D256@Thickness 6.35 mm, Temperature 0.000 °CJ/m
Izod impact strength (notched)80.1ASTM D256@Thickness 3.17 mm, Temperature 23.0 °CJ/m
Optical Properties
Transmittance77ASTM D1003;Visible%
gloss113At 60°; ASTM D1003%
Haze10.2ASTM D1003%
Thermal Properties
Heat Deflection temperature85ASTM D648; at 1.8 MPa°C
Vicat softening temperature104ASTM D1525°C
Physical Properties
Melting range204 – 246°C
Processing Properties
MFI7.9ASTM D1238@Load 5.00 kg, Temperature 230 °Cg/10min
Mold Temperature32.2 – 60°C
Dry Time180 – 240min
Drying Temperature82.23-4hrs°C
Electrical Properties
Volume resistance89,000,000,00012% RH; ASTM D257-78ohm-cm
Surface Resistance2,600,000,00012% RH; ASTM EOS/ESD 511.11ohm
Volume resistance180,000,000,000After 24 hours Cold Water Showering; ASTM D257-78ohm-cm
Surface Resistance2,700,000,000After 24 hours Cold Water Showering; ASTM FTM 101Cohm