Specifications
PropertyValueUnit
Processing Properties
Middle Barrel Temperature221°C
MFI12ASTM D1238@Load 5.00 kg, Temperature 230 °Cg/10min
Mold Temperature48.9°C
Dry Time180 – 240min
Drying Temperature71.13-4hrs°C
Linear Mold Shrinkage0.004 – 0.007ASTM D551cm/cm
Thermal Properties
Thermal Expansion72ASTM D696@Temperature 0.000 -100 °C;Linearum/(m-°C)
Heat Deflection temperature68.9ASTM D648; at 1.8 MPa°C
Vicat softening temperature88ASTM D1525°C
FlameabilityHB
Mechanical Properties
Flexural modulus-MD1,400ASTM D790MPa
Elongation at break-MD27ASTM D638%
Tensile Stress at yield-MD34.5ASTM D638MPa
Tensile modulus-MD1,700ASTM D638MPa
Rockwell Hardness40Rockwell L; ASTM D785
Elongation at yield4.3ASTM D638%
Flexural strength55.8ASTM D790MPa
Physical Properties
Specific Gravity1.07ASTM D792
Melting point227°C
Chemical Properties
Water absorption<0.30ASTM D570%
Optical Properties
Haze2ASTM D1003%
Transmittance88ASTM D1003;Visible%
Appearance Properties
Refractive index1.52ASTM D542