Specifications
PropertyValueUnit
Thermal Properties
Thermal Conductivity0.19DIN 52612W/(m K)
U Value4.4DIN 4701; for 10 mmW/m2
Heat Deflection temperature105ISO 75;at 1.8 MPa°C
Maximum Service Temperature80Permanent°C
Specific Heat Capacity1.47J/(g °C)
Thermal Expansion70DIN 53752A@Temperature 0.000-50.0 °C;Linearum/(m-°C)
Vicat softening temperature115ISO 306, Method B 50°C
FlameabilityHB@Thickness 1.60 mm
U Value5.8DIN 4701; for 1 mmW/m2
Heat Deflection temperature113ISO 75;at 0.46 MPa°C
Maximum Service Temperature200IR Radiator°C
U Value5.6DIN 4701; for 3 mmW/m2
U Value5.3DIN 4701; for 5 mmW/m2
Optical Properties
Absorption in the Visible Range<0.05clear grade, 3 mm%
Reflection Coefficient0.04(clear grade, Reflection loss in the visible range (for each surface) @Thickness 3.00 mm;Visible(0-1
Transmittance0UV ; clear grade@Thickness 3.00 mm%
Transmittance92clear grade; DIN 5036, Part 3@Thickness 3.00 mm;Visible%
Transmittance85clear grade, 3 mm, DIN EN 410%
Mechanical Properties
Tensile Stress at break-MD110ISO 527-2/1B/5@Temperature -40.0 °CMPa
Ball indentation Hardness175H961/30; ISO 2039-1MPa
Flexural strength1155mm/min (80x10x4 mm); ISO 178MPa
Abrasion20 – 30℅Haze, Abrasion resistance in Taber abrader test (100 rev.;5.4 N; CS-10F) ; ISO 9352
Tensile strength40ISO 527-2/1B/5@Temperature 70.0 °C;UltimateMPa
(Charpy Impact Strength(unnotched15ISO 179/1fUkJ/m2
Elongation at break-MD5.5ISO 527-2/1B/5
Electrical Properties
Volume resistance>1.00e+15DIN VDE 0303, Part 3ohm-cm
Surface Resistance50,000,000,000,000DIN VDE 0303, Part 3ohm
Dielectric Strength30DIN VDE 0303, Part 2kV/mm
Comparative Tracking Index600DIN VDE 0303, Part 1V
Dissipation Factor0.06DIN VDE 0303, Part 4@Frequency 50 Hz
Dielectric Constant3.6DIN VDE 0303, Part 4@Frequency 50 Hz
Shielding Effectiveness30Weighted Sound Reduction Index at 6 mm
Physical Properties
Density1.19ISO 1183g/mL
Permeability2.0e-14to O2g-cm/(cm2-h-Pa)
Moisture Expansion0.5Possible Expansion due to heat and moisture%
flash point425Ignition Temperature; DIN 51794°C
Permeability4.5e-15to N2g-cm/(cm2-h-Pa)
Permeability8.3e-15to Airg-cm/(cm2-h-Pa)
Permeability1.1e-13to CO2g-cm/(cm2-h-Pa)
Chemical Properties
Water absorption2.1Max. Weight Gain During Immersion; ISO 62, Method 1; at Saturation%
Moisture Vapor Transmission55cc-mm/(m2-24h-atm)
Water absorption0.4824hrs, 23°C from dry state; ISO 62, Method 1%
Appearance Properties
Refractive index1.491clear grade; ISO 489@Thickness 3.00 mm