Specifications
PropertyValueUnit
Thermal Properties
Vicat softening temperature105B50; ISO 306°C
Thermal Expansion63ASTM E831@Temperature 0.000 -50.0 °C;Linearum/(m-°C)
Heat Deflection temperature101ISO 75; at 0.46 MPa°C
Glass transition Temperature106IEC 10006°C
Heat Deflection temperature97ISO 75; at 1.8 MPa°C
Mechanical Properties
Tensile modulus-MD3,4001mm/min; ISO 527MPa
Elongation at break-MD65mm/min; ISO 527%
Tensile Stress at break-MD705mm/min; ISO 527MPa
(Charpy Impact Strength(unnotched20ISO 179@Temperature 23.0 °CkJ/m2
Optical Properties
Transmittance81Transmission Factor; DIN 5036;Visible%
Physical Properties
Density1.19ISO 1183g/mL
Melting range220 – 260°C
Processing Properties
MFI1.1305ISO 1133@Load 3.80 kg, Temperature 230 °Cg/10min
Die Temperature220 – 260°C
Drying Temperature<95.0Predrying°C
Dry Time120 – 180Desiccant-type driermin
Electrical Properties
Glow WireTest700°C