Specifications
PropertyValueUnit
Processing Properties
Drying Temperature<95.0Predrying°C
Dry Time120 – 180Desiccant-type driermin
Mold Temperature60 – 90°C
MFI2.975ISO 1133@Load 3.80 kg, Temperature 230 °Cg/10min
Physical Properties
Melting range220 – 260°C
Density1.19ISO 1183g/mL
Thermal Properties
Glass transition Temperature111IEC 10006°C
Vicat softening temperature109B50; ISO 306°C
Thermal Expansion63ASTM E831@Temperature 0.000 -50.0 °C;Linearum/(m-°C)
Heat Deflection temperature103ISO 75; at 0.46 MPa°C
Heat Deflection temperature98ISO 75; at 1.8 MPa°C
Optical Properties
Transmittance87Transmission Factor; DIN 5036;Visible%
Mechanical Properties
Tensile modulus-MD3,3001mm/min; ISO 527MPa
Elongation at break-MD4.55mm/min; ISO 527%
Tensile Stress at break-MD715mm/min; ISO 527MPa
(Charpy Impact Strength(unnotched18ISO 179@Temperature 23.0 °CkJ/m2