Specifications
PropertyValueUnit
Thermal Properties
Vicat softening temperature108B50; ISO 306°C
Thermal Expansion80ASTM E831@Temperature 0.000 -50.0 °C;Linearum/(m-°C)
Heat Deflection temperature103ISO 75;at 0.46 MPa°C
Glass transition Temperature117IEC 10006°C
FlameabilityHBIEC 707@Thickness 1.60 mm
Heat Deflection temperature98ISO 75;at 1.8 MPa°C
Mechanical Properties
Tensile modulus-MD3,3001mm/min; ISO 527MPa
Tensile Stress at break-MD775mm/min; ISO 527MPa
Elongation at break-MD5.55mm/min; ISO 527%
(Charpy Impact Strength(unnotched20ISO 179@Temperature 23.0 °CkJ/m2
Optical Properties
Transmittance92Transmission Factor; DIN 5036;Visible%
Haze<0.50ASTM D1003%
Physical Properties
Density1.19ISO 1183g/mL
Melting range220 – 260°C
Appearance Properties
Refractive index1.49ISO 489
Processing Properties
MFI3.57ISO 1133@Load 3.80 kg, Temperature 230 °Cg/10min
Mold Temperature60 – 90°C
Drying Temperature<98.0Predrying°C
Dry Time120 – 180Desiccant-type driermin