Specifications
PropertyValueUnit
Processing Properties
Drying Temperature<93.0Predrying°C
Mold Temperature60 – 90°C
MFI7.14ISO 1133@Load 3.80 kg, Temperature 230 °Cg/10min
Dry Time120 – 180Desiccant-type driermin
Physical Properties
Melting range220 – 260°C
Density1.19ISO 1183g/mL
Mechanical Properties
(Charpy Impact Strength(unnotched20ISO 179@Temperature 23.0 °CkJ/m2
Elongation at break-MD3.55mm/min; ISO 527%
Tensile Stress at break-MD735mm/min; ISO 527MPa
Tensile modulus-MD3,2001mm/min; ISO 527MPa
Appearance Properties
Refractive index1.49ISO 489
Thermal Properties
Thermal Expansion80ASTM E831@Temperature 0.000 -50.0 °C;Linearum/(m-°C)
Vicat softening temperature103B50; ISO 306°C
Heat Deflection temperature100ISO 75;at 0.46 MPa°C
Glass transition Temperature110IEC 10006°C
FlameabilityHBIEC 707@Thickness 1.60 mm
Heat Deflection temperature95ISO 75;at 1.8 MPa°C
Optical Properties
Transmittance92Transmission Factor; DIN 5036;Visible%
Haze<0.50ASTM D1003%