Specifications
PropertyValueUnit
Optical Properties
Haze<0.50ASTM D1003%
Transmittance92Transmission Factor; DIN 5036;Visible%
Thermal Properties
FlameabilityHBIEC 707@Thickness 1.60 mm
Glass transition Temperature112IEC 10006°C
Heat Deflection temperature95ISO 75;at 1.8 MPa°C
Vicat softening temperature103B50; ISO 306°C
Thermal Expansion80ASTM E831@Temperature 0.000 -50.0 °C;Linearum/(m-°C)
Heat Deflection temperature100ISO 75;at 0.46 MPa°C
Mechanical Properties
Tensile modulus-MD3,2001mm/min; ISO 527MPa
Tensile Stress at break-MD765mm/min; ISO 527MPa
Elongation at break-MD5.55mm/min; ISO 527%
(Charpy Impact Strength(unnotched20ISO 179@Temperature 23.0 °CkJ/m2
Physical Properties
Density1.19ISO 1183g/mL
Melting range220 – 260°C
Appearance Properties
Refractive index1.49ISO 489
Processing Properties
MFI1.67ISO 1133@Load 3.80 kg, Temperature 230 °Cg/10min
Drying Temperature<93.0Predrying°C
Dry Time120 – 180Desiccant-type driermin
Die Temperature220 – 260°C