Specifications
PropertyValueUnit
Mechanical Properties
Izod impact strength (notched)26.7BAR; ASTM D256@Diameter 6.35 mm,Temperature 0.000 °CJ/m
Flexural modulus-MD2,830ASTM D790MPa
Elongation at break-MD8ASTM D638%
Tensile Stress at break-MD62.1ASTM D638MPa
Tensile modulus-MD2,960ASTM D638MPa
Rockwell Hardness60Rockwell M; ASTM D785
Elongation at yield3ASTM D638%
Flexural strength110ASTM D790MPa
Izod impact strength (notched)37.4bar; ASTM D256@Diameter 3.17 mmJ/m
Izod impact strength (notched)37.4BAR; ASTM D256@Diameter 6.35 mmJ/m
Processing Properties
Middle Barrel Temperature193 – 246Cylinder Temp°C
MFI6ASTM D1238@ Temperature 230 °Cg/10min
Drying Temperature79.4°C
Mold Temperature43.3 – 65.6°C
Dry Time180 – 240min
Linear Mold Shrinkage0.004 – 0.007ASTM D951cm/cm
MFI6ASTM D1238@Load 5.00 kgg/10min
Thermal Properties
Thermal Expansion72linear;ASTM D696@Temperature 0.000 -100 °Cum/(m-°C)
Heat Deflection temperature82.2Annealed; ASTM D648@Thickness 6.35 mm; at 1.8 MPa°C
Vicat softening temperature96.1ASTM D1525°C
Physical Properties
Specific Gravity1.11ASTM D792
Melting range204 – 246°C
Bulk density0.65ASTM D1895g/mL
Optical Properties
Transmittance90visible; ASTM D1003%
Haze3ASTM D1003%
Chemical Properties
Water absorption<0.30ASTM D570%