Specifications
PropertyValueUnit
Mechanical Properties
Rockwell Hardness89Rockwell M; ASTM D785
Tensile modulus-MD3,240ASTM D638MPa
Tensile Stress at break-MD63.4ASTM D638MPa
Elongation at break-MD2 – 4ASTM D638%
Elongation at yield2 – 4ASTM D638%
Flexural strength107ASTM D790MPa
Flexural modulus-MD3,170ASTM D790MPa
Izod impact strength (notched)19.2BAR; ASTM D256@Diameter 6.35 mmJ/m
Processing Properties
Linear Mold Shrinkage0.003 – 0.006ASTM D951cm/cm
Dry Time180 – 240min
Drying Temperature79.4°C
Mold Temperature32.2 – 79.4°C
MFI24ASTM D1238@Temperature 230 °Cg/10min
Middle Barrel Temperature210 – 243Cylinder Temp°C
MFI24ASTM D1238@Load 3.80 kgg/10min
Chemical Properties
Water absorption<0.30ASTM D570%
Physical Properties
Bulk density0.66ASTM D1895g/mL
Melting range210 – 243°C
Specific Gravity1.19ASTM D792
Thermal Properties
Vicat softening temperature90ASTM D1525°C
Heat Deflection temperature82.2Annealed; ASTM D648@Thickness 6.35 mm; at 1.8 MPa°C
Thermal Expansion72ASTM D696@Temperature 0.000 -100 °C;linearum/(m-°C)
Appearance Properties
Refractive index1.49ASTM D542
Optical Properties
Transmittance92ASTM D1003;visible%
Haze<1.0ASTM D1003%
Yellow index<1.0ASTM D1925