Specifications
PropertyValueUnit
Mechanical Properties
Elongation at yield4 – 6ASTM D638%
Tensile Stress at break-MD77.9ASTM D638MPa
Flexural modulus-MD3,450ASTM D790MPa
Flexural strength112ASTM D790MPa
Tensile modulus-MD3,240ASTM D638MPa
Elongation at break-MD4 – 6ASTM D638%
Rockwell Hardness95Rockwell M;ASTM D785
Izod impact strength (notched)19.2BAR; ASTM D256@Diameter 6.35 mmJ/m
Physical Properties
Melting range241 – 252°C
Specific Gravity1.19ASTM D792
Bulk density0.66ASTM D1895g/mL
Chemical Properties
Water absorption<0.30ASTM D570%
Optical Properties
Transmittance92ASTM D1003;visible%
Yellow index<1.0ASTM D1925
Haze<1.0ASTM D1003%
Thermal Properties
Vicat softening temperature117ASTM D1525°C
Heat Deflection temperature100Annealed; ASTM D648@Thickness 6.35 mm;at 1.8 MPa°C
Thermal Expansion72ASTM D696@Temperature 0.000-100.0 °C;linearum/(m-°C)
Processing Properties
MFI3.4ASTM D1238@Load 3.80 kg, Temperature 230 °Cg/10min
Linear Mold Shrinkage0.004 – 0.007ASTM D951cm/cm
Mold Temperature37.8 – 79.4°C
Middle Barrel Temperature241 – 252Cylinder Temp°C
Drying Temperature79.4°C
Dry Time180 – 240min
Appearance Properties
Refractive index1.49ASTM D542