Specifications
PropertyValueUnit
Mechanical Properties
Elongation at yield2 – 4ASTM D638%
Tensile Stress at break-MD68.3ASTM D638MPa
Flexural modulus-MD3,170ASTM D790MPa
Flexural strength94.5ASTM D790MPa
Tensile modulus-MD3,310ASTM D638MPa
Elongation at break-MD2 – 4ASTM D638%
Rockwell Hardness94Rockwell M;ASTM D785
Izod impact strength (notched)18.2BAR; ASTM D256@Diameter 6.35 mmJ/m
Chemical Properties
Water absorption<0.30ASTM D570%
Optical Properties
Transmittance92ASTM D1003;visible%
Haze<1.0ASTM D1003%
Yellow index<1.0ASTM D1925
Thermal Properties
Vicat softening temperature102ASTM D1525°C
Heat Deflection temperature98.9Annealed; ASTM D648@Thickness 6.35 mm;at 1.8 MPa°C
Thermal Expansion72ASTM D696@Temperature 0.000-100.0 °C;linearum/(m-°C)
Physical Properties
Specific Gravity1.19ASTM D792
Bulk density0.66ASTM D1895g/mL
Melting range221 – 249°C
Processing Properties
MFI6.4ASTM D1238@Load 3.80 kg, Temperature 230 °Cg/10min
Linear Mold Shrinkage0.004 – 0.007ASTM D951cm/cm
Middle Barrel Temperature221 – 249Cylinder Temp°C
Mold Temperature32.2 – 79.4°C
Drying Temperature76.7°C
Dry Time180 – 240min