Specifications
PropertyValueUnit
Processing Properties
Dry Time180 – 240min
Drying Temperature79.4°C
Mold Temperature32.2 – 79.4°C
MFI1.3ASTM D1238@Load 3.80 kg, Temperature 230 °Cg/10min
Linear Mold Shrinkage0.004 – 0.007ASTM D951cm/cm
Middle Barrel Temperature220 – 260Cylinder Temp°C
Mechanical Properties
Elongation at yield4 – 6ASTM D638%
Tensile Stress at break-MD89.29ASTM D638MPa
Flexural modulus-MD3,310ASTM D790MPa
Flexural strength123.9ASTM D790MPa
Tensile modulus-MD3,650ASTM D638MPa
Elongation at break-MD4 – 6ASTM D638%
Rockwell Hardness94Rockwell M;ASTM D785
Chemical Properties
Water absorption<0.30ASTM D570%
Optical Properties
Transmittance92ASTM D1003;visible%
Haze<1.0ASTM D1003%
Yellow index<1.0ASTM D1925
Thermal Properties
Vicat softening temperature103ASTM D1525°C
Heat Deflection temperature100Annealed; ASTM D648@Thickness 6.35 mm;at 1.8 MPa°C
Thermal Expansion72ASTM D696@Temperature 0.000-100.0 °C;linearum/(m-°C)
Physical Properties
Specific Gravity1.19ASTM D792
Bulk density0.66ASTM D1895g/mL
Melting range220 – 260°C
Appearance Properties
Refractive index1.49ASTM D542