Specifications
PropertyValueUnit
Thermal Properties
Specific Heat Capacity2.3@Temperature 175 °CJ/(g °C)
Heat Deflection temperature82ASTM D648;at 1.8 MPa°C
Vicat softening temperature98ASTM D1525°C
Thermal Conductivity0.22W/(m K)
Thermal Expansion83ASTM D696@Temperature 20.0 °Cum/(m-°C)
Specific Heat Capacity1.9@Temperature 100 °CJ/(g °C)
Specific Heat Capacity1.3@Temperature 25.0 °CJ/(g °C)
Mechanical Properties
Elongation at yield3.5ASTM D638%
Tensile strength38ASTM D638;ultimateMPa
Izod impact strength (notched)130bar; ASTM D256@Diameter 6.35 mmJ/m
Elongation at break-MD8.3ASTM D638%
Tensile modulus-MD2,100ASTM D638MPa
Flexural strength62ASTM D790; at YieldMPa
Flexural modulus-MD2,000ASTM D790MPa
Physical Properties
Density1.11ASTM D792g/mL
Bulk density0.65ASTM D1895;Apparent Bulk Densityg/mL
Optical Properties
Haze12ASTM D1003%
Transmittance88ASTM D1003;visible%
Processing Properties
MFI8ASTM D1238@Load 5.00 kg, Temperature 230 °Cg/10min
Linear Mold Shrinkage0.004 – 0.007ASTM D551cm/cm