Specifications
PropertyValueUnit
Optical Properties
Reflection Coefficient0.04Visible (0-1); clear grade, Reflection loss in the visible range (for each surface) @Thickness 3.00 mm;
Transmittance0UV; clear grade@Thickness 3.00 mm%
Absorption in the Visible Range<0.05clear grade, 3 mm%
Transmittance91Visible; clear grade; DIN 5036, Part 3@Thickness 3.00 mm;visible%
Transmittance85Total Energy Transmittance g; clear grade, 3 mm, DIN EN 410%
Mechanical Properties
Poisson\'s ratio0.41dilation speed of 5% per min; up to 2% dilation; ISO 527-1@Temperature 23.0 °C
(Charpy Impact Strength(unnotched75ISO 179/1fUkJ/m2
Charpy Impact Strength (notched)7.5ISO 179/1eAkJ/m2
Ball indentation Hardness120H961/30; ISO 2039-1MPa
Abrasion30 – 40% Haze, Abrasion resistance in Taber abrader test (100 rev.;5.4 N; CS-10F); ISO 9352
(Izod impact strength(notched6ISO 180/1AkJ/m2
Flexural strength775 mm/min (80x10x4 mm); ISO 178
Processing Properties
Processing Temperature140 – 150Forming Temperature°C
Processing Temperature>75.0Reverse Forming Temperature°C
Thermal Properties
U Value5.6DIN 4701; for 3 mmW/m2
Heat Deflection temperature92ISO 75;at 1.8 MPa°C
Maximum Service Temperature70Permanent;air°C
Specific Heat Capacity1.47J/(g °C)
Thermal Expansion90DIN 53752A@Temperature 0.000-50.0 °C;linearum/(m-°C)
Vicat softening temperature100ISO 306, Method B 50°C
Heat Deflection temperature96ISO 75;at 0.46 MPa°C
Physical Properties
Moisture Expansion0.6Possible Expansion due to heat and moisture%
Density1.19ISO 1183g/mL
Chemical Properties
Water absorption2.1Max. Weight Gain During Immersion; ISO 62, Method 1; at Saturation%
Water absorption0.53724 hrs, 23°C from dry state; ISO 62, Method 1%
Electrical Properties
Volume resistance>1.00e+14DIN VDE 0303, Part 3ohm-cm
Surface Resistance>1.00e+14DIN VDE 0303, Part 3ohm
Appearance Properties
Refractive index1.491clear grade; ISO 489@Thickness 3.00 mm