Vestamid® DX9322 Black 15% Glass Reinforced Nylon 612(Dry as Molded) | Metasan
Home
/
Products
/
Polyamides
/
Glass fiber
/ Vestamid® DX9322 Black 15% Glass Reinforced Nylon 612(Dry as Molded)
Vestamid® DX9322 Black 15% Glass Reinforced Nylon 612(Dry as Molded)
این ماده گریدی از نایلون بوده که حاوی 15% الیاف شیشه آسیاب شده است .
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
Applications
بدنه های در معرض ضربه درپوش ها
Advantages
پایداری حرارتی خوب تاب برداشتگی کم قطعه
Handling
داده های این ماده بعد از قالب گیری(در شرایط خشک, رطوبت کمتر از 0.2% ) به دست آمده است.
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Mechanical Properties
Elongation at yield
8
ISO 527-2/1A
%
Elongation at break-MD
18
ISO 527-2/1A
%
Tensile Stress at break-MD
59
ISO 527-2/1A
MPa
Charpy Impact Strength (notched)
3
ISO 179/1eA@Temperature -30.0 °C
kJ/m2
(Charpy Impact Strength(unnotched
46
ISO 179/1eU@Temperature 23.0 °C
kJ/m2
Tensile modulus-MD
3,050
ISO 527-2/1A
MPa
Tensile Stress at yield-MD
63
ISO 527-2/1A
MPa
Charpy Impact Strength (notched)
4
ISO 179/1eA@Temperature 23.0 °C
kJ/m2
(Charpy Impact Strength(unnotched
43
ISO 179/1eU@Temperature -30.0 °C
kJ/m2
Electrical Properties
Dielectric Constant
3.1
IEC 60250@Frequency 1e+6 Hz
Comparative Tracking Index
575
Test Solution A, 100 drops; IEC 60112
V
Volume resistance
100,000,000,000,000
IEC 60093
ohm-cm
Dissipation Factor
0.0493
IEC 60250@Frequency 1e+6 Hz
Dielectric Constant
4.3
IEC 60250@Frequency 100 Hz
Comparative Tracking Index
>600
Test Solution A, 50 drops; IEC 60112
V
Dissipation Factor
0.043
IEC 60250@Frequency 100 Hz
Thermal Properties
Thermal Expansion
60
ISO 11359@Temperature 23.0 -55.0 °C, Transverse to Flow
um/(m-°C)
Flameability
HB
@Thickness 1.60 mm
Heat Deflection temperature
186
ISO 75- at 0.46 MPa
°C
Vicat softening temperature
193
50N; ISO 306
°C
Heat Deflection temperature
114
ISO 75- at 1.8 MPa
°C
Thermal Expansion
100
Longitudinal; ISO 11359 @Temperature 23.0 - 55.0 °C
um/(m-°C)
Physical Properties
Density
1.17
ISO 1183
g/mL
Moisture absorption
0.9
23°C/50% R.H.; ISO 62-at Equilibrium
%
Melting point
215
Peak Temperature; ISO 11357
°C
Processing Properties
Linear Mold Shrinkage
0.0093
127x12.7x3.2 mm (processing cond. acc. To ISO 1874-2), Transverse
cm/cm
Linear Mold Shrinkage
0.0192
127x12.7x3.2 mm (processing cond. acc. To ISO 1874-2)
cm/cm
Chemical Properties
Water absorption
2.4
ISO 62-at Saturation
%