Vestamid® DX9320 Black 10% Glass Reinforced Nylon 612(Dry as Molded) | Metasan
Home
/
Products
/
Polyamides
/
Glass fiber
/ Vestamid® DX9320 Black 10% Glass Reinforced Nylon 612(Dry as Molded)
Vestamid® DX9320 Black 10% Glass Reinforced Nylon 612(Dry as Molded)
این ماده گریدی از نایلون بوده که با 10% الیاف شیشه تقویت شده است و ویسکوزیته متوسطی دارد.
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
Applications
بدنه های در معرض ضربه درپوش
Advantages
مقاوم به ضربه پایداری حرارتی خوب
Handling
داده های این ماده بعد از قالب گیری(در شرایط خشک, رطوبت کمتر از 0.2% ) به دست آمده است.
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Electrical Properties
Comparative Tracking Index
600
Test Solution A, 100 drops; IEC 60112
V
Volume resistance
100,000,000,000,000
IEC 60093
ohm-cm
Dielectric Constant
3.1
IEC 60250@Frequency 1e+6 Hz
Dissipation Factor
0.0466
IEC 60250@Frequency 1e+6 Hz
Dissipation Factor
0.047
IEC 60250@Frequency 100 Hz
Comparative Tracking Index
>600
Test Solution A, 50 drops; IEC 60112
V
Dielectric Constant
4.3
IEC 60250@Frequency 100 Hz
Mechanical Properties
Tensile Stress at break-MD
82
ISO 527-2/1A
MPa
Elongation at break-MD
10
ISO 527-2/1A
%
(Charpy Impact Strength(unnotched
81
ISO 179/1eU@Temperature 23.0 °C
kJ/m2
Tensile modulus-MD
3,700
ISO 527-2/1A
MPa
Charpy Impact Strength (notched)
5
ISO 179/1eA@Temperature -30.0 °C
kJ/m2
Elongation at yield
5
%
Charpy Impact Strength (notched)
11
ISO 179/1eA@Temperature 23.0 °C
kJ/m2
(Charpy Impact Strength(unnotched
69
ISO 179/1eU@Temperature -30.0 °C
kJ/m2
Thermal Properties
Thermal Expansion
80
ISO 11359@Temperature 23.0 -55.0 °C, Transverse to Flow
um/(m-°C)
Heat Deflection temperature
201
ISO 75- at 0.46 MPa
°C
Vicat softening temperature
199
50N; ISO 306
°C
Flameability
HB
@Thickness 1.60 mm
Heat Deflection temperature
183
ISO 75- at 1.8 MPa
°C
Thermal Expansion
70
Longitudinal; ISO 11359 @Temperature 23.0 - 55.0 °C
um/(m-°C)
Physical Properties
Melting point
215
Peak Temperature; ISO 11357
°C
Density
1.12
ISO 1183
g/mL
Moisture absorption
1
23°C/50% R.H.; ISO 62;at Equilibrium
%
Processing Properties
Linear Mold Shrinkage
0.0097
127x12.7x3.2 mm (processing cond. acc. To ISO 1874-2), Transverse
cm/cm
Linear Mold Shrinkage
0.0129
127x12.7x3.2 mm (processing cond. acc. To ISO 1874-2)
cm/cm
Chemical Properties
Water absorption
2.6
ISO 62;at Saturation
%